Experimental study and modelling of the phase transformation of Zircaloy-4 alloy under high thermal transients

Résumé

Dilatometry tests were performed to study the phase transformation kinetic of nuclear fuel claddings made of Zircaloy-4 upon fast heating rates (up to 2000 °C/s). These tests highlighted that from equilibrium to 500 °C/s the temperature at which the transformation starts shifts towards higher temperatures with increasing heating rates. Above 500 °C/s, no impact of the heating rate was observed. The temperature at which the transformation ends remains close to 960 °C with no clear dependence on heating rate. Metallurgical analyses were carried out and were in agreement with the results obtained by dilatometry. A phase transition model was identified from equilibrium to 2000 °C/s.
Fichier principal
Vignette du fichier
Jailin_2020_MatChar.pdf (6.52 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02489746 , version 1 (24-02-2020)
hal-02489746 , version 2 (12-07-2022)

Licence

Paternité - Pas d'utilisation commerciale - Pas de modification

Identifiants

Citer

T. Jailin, Nicolas Tardif, J. Desquines, Michel Coret, M.-C. Baietto, et al.. Experimental study and modelling of the phase transformation of Zircaloy-4 alloy under high thermal transients. Materials Characterization, 2020, 162, pp.110199. ⟨10.1016/j.matchar.2020.110199⟩. ⟨hal-02489746v1⟩
99 Consultations
143 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More